TRIBOCOMP® POM TS0
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DhI19y_TRIBOCOMP-POM-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRIBOCOMP®POM TS0 is a polyoxymethylene (POM) copolymer product, which contains a filler of 20% ptfe fiber. It is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 2.2 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 50.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| Dynamic | 0.14 | ASTM D3702 | |
| Static | 0.080 | ASTM D3702 | |
| Wear Factor | 18.0 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 105 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 1.0E-4 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.23 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 160 - 210 | °C | |
| Middle Temperature | 170 - 220 | °C | |
| Front Temperature | 180 - 220 | °C | |
| Nozzle Temperature | 200 - 225 | °C | |
| Processing (Melt) Temp | < 220 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 200.5 | RTP Company | Nylon 66 | RTP |
| Dynaflex™ G7940-9 NSFG | PolyOne Corporation | TPE | Dynaflex™ |
| Haysite BMC 270FRII | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| Kostrate® EDGE YP | Plastic Selection Group, Inc. | TP, Unspecified | Kostrate® EDGE |
| Sylvin 8999-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |