Bio-Flex® S 9533
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dh4QEL_Bio-Flex-S-9533.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bio-Flex® S 9533 Biodegradable compound for injection moulding. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 24 - 28 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4580 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 50.0 | MPa | ISO 527-2 |
| Fracture | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 8.0 | % | ISO 527-2 |
| Flexural Modulus | 4700 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | 4.0 | % | ISO 527-2 |
| Flexural Strain at Break | 3 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 37 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 63.0 | °C | ISO 306 |
| Melting Temperature (DSC) | 150 - 170 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 150 | °C | |
| Middle Temperature | 160 | °C | |
| Front Temperature | 175 | °C | |
| Nozzle Temperature | 180 | °C | |
| Mold Temperature | 30.0 - 65.0 | °C |
| Injection instructions |
|---|
| Holding pressure level: 40 - 70%Melt cushion (of volume): 3 - 10%Cooling time: 15 secmax. Dwell time: 300 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adsyl 5 C 39 F ST | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| LARIPUR® LPR 9060EF | COIM S.p.A. | TPU-Polyether | LARIPUR® |
| INSTRUC PPSGF15 | Infinity LTL Engineered Compounds | PPS | INSTRUC |
| LNP™ STAT-KON™ ZE004 compound | SABIC Innovative Plastics Asia Pacific | Polyphenylene, Unspecified | LNP™ STAT-KON™ |
| OmniLon™ PA6/6 MF40 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |