LNP™ LUBRICOMP™ QFL17RS compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DgdRqu_LNP-LUBRICOMP-QFL17RS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* QFL17RS is a compound based on Nylon 6/10 resin containing 35% Glass Fiber, 5% PTFE. Added features of this material include: Easy Release, Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound QFL-4017 ER HS Product reorder name: QFL17RS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.73 | % | ISO 294-4 |
| Flow : 24 hr | 0.15 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.19 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11900 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 192 | MPa | ASTM D638 |
| Break | 183 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.5 | % | ASTM D638 |
| Break | 3.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9030 | MPa | ASTM D790 |
| -- | 9800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 283 | MPa | ASTM D790 |
| -- | 273 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 180 | J/m | ASTM D256 |
| 23°C 2 | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1400 | J/m | ASTM D4812 |
| 23°C 3 | 88 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.8 | J | ASTM D3763 |
| -- | 4.76 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 223 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 214 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 208 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 5.9E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V972 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 1400 P TFE 10 | RTP Company | PPSU | RTP |
| Thermylene® P4-10TC-0520 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| TULAMID® PA-1AP | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| Unipren® Elastomers D3 PRTA011 60A IG06S1 UP345 | Petropol Industry and Trade of Polymers LTDA | TPO (POE) | Unipren® Elastomers |