Ecomass® 3011ZD86
| Category: | PC , Polycarbonate |
| Manufacturer: | Ecomass Technologies |
| Trademark: | Ecomass® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DgLT67_Ecomass-3011ZD86.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ecomass® 3011ZD86 is a Polycarbonate (PC) material filled with tungsten. It is available in North America for injection molding. Important attributes of Ecomass® 3011ZD86 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 6.00 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 5920 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 7.4 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 138 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 132 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 315 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2300 A | RTP Company | PUR, Unspecified | RTP |
| SIBUR Synthetic Rubber BR-1243 Nd Grade A | SIBUR, LLC | PBR, High Cis | SIBUR Synthetic Rubber |
| Daelim Po1y庐 LD-08 | DAELIM INDUSTRIAL CO., LTD. | LDPE | Daelim Po1y® |
| MAJ'ECO DP484W - 8716 | AD majoris | PP Copolymer | MAJ'ECO |
| MAJORIS DFR 247 | AD majoris | PP, Unspecified | MAJORIS |