PRIMACOR™ 1430
| Category: | EAA , Copolymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | PRIMACOR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DfdHfU_PRIMACOR-1430.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
PRIMACOR™ 1430 is an ethylene acrylic acid copolymer that provides good sealability, hot tack and excellent adhesion to polar (foil, nylon, etc.) materials. It also provides excellent toughness, clarity and tear resistance.
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238, ISO 1133 |
| Comonomer Content 2 | 9.7 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, molding 3 | 7.67 | MPa | ASTM D638 |
| Yield, molding | 7.67 | MPa | ISO 527-2/508 |
| Fracture, molding 4 | 19.5 | MPa | ASTM D638 |
| Fracture, molding | 19.5 | MPa | ISO 527-2/508 |
| Tensile Elongation | |||
| Fracture, molding 5 | 580 | % | ASTM D638 |
| Fracture, molding | 580 | % | ISO 527-2/508 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| MD : Yield, 51 µm | 10.4 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 10.2 | MPa | ASTM D882 |
| MD : Yield, 51 µm | 10.4 | MPa | ISO 527-3 |
| TD : Yield, 51 µm | 10.2 | MPa | ISO 527-3 |
| MD : Fracture, 51 µm | 30.6 | MPa | ASTM D882, ISO 527-3 |
| TD : Fracture, 51 µm | 31.0 | MPa | ASTM D882, ISO 527-3 |
| Tensile Elongation | ASTM D882, ISO 527-3 | ||
| MD : Fracture, 51 µm | 420 | % | ASTM D882, ISO 527-3 |
| TD : Fracture, 51 µm | 470 | % | ASTM D882, ISO 527-3 |
| Elmendorf Tear Strength 6 | |||
| MD : 51 µm | 470 | g | ASTM D1922 |
| TD : 51 µm | 730 | g | ASTM D1922 |
| MD : 51 µm | 2100 | N | ISO 6383-2 |
| TD : 51 µm | 3300 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 76.1 | °C | ASTM D1525, ISO 306 |
| Melting Temperature (DSC) | 96.1 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 74 | ASTM D2457 | |
| Haze | |||
| 50.8 µm | 4.0 | % | ISO 14782 |
| 50.8 µm | 4.0 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 挤出涂层薄膜的制造条件：用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆类型：带 Maddock Mixer 的单跨型 模具间隙：40 密尔 (1.0 mm) 熔体温度：384°F (196°C) 输出：模具周长的 6 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 冷冻线高度：29 英寸 (737 mm) |
| Note Message | |
|---|---|
| 1 . | As measured during production. |
| 2 . | The comonomer content measured by Dow attribute method has the same accuracy as ASTM D 4094. |
| 3 . | 510 mm/min |
| 4 . | 510 mm/min |
| 5 . | 510 mm/min |
| 6 . | The comonomer content measured by Dow attribute method has the same accuracy as ASTM D 4094. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP240T | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Tritan™ MX810 | Eastman Chemical Company | Copolyester | Tritan™ |
| Adflex X 500 F | LyondellBasell Industries | Polyolefin, Unspecified | Adflex |
| HANWHA LLDPE 3305 | Hanwha Chemical | LLDPE | HANWHA LLDPE |
| Hostaform® C 13021 10/1570 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |