DENKA ABS K-5120G
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DexlhG_DENKA-ABS-K-5120G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DENKA ABS K-5120G is an Acrylonitrile Butadiene Styrene (ABS) product filled with 20% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.21 | g/cm³ | ASTM D792 |
| 23°C | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 0.40 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.10 to 0.30 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 122 | ASTM D785 | |
| R-Scale | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 77.0 | MPa | ASTM D638 |
| -- | 6050 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 88.0 | MPa | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 4700 | MPa | ASTM D790 |
| -- 3 | 5800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 108 | MPa | ASTM D790 |
| -- 5 | 141 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Notched Izod Impact | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 6 | 129 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 134 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ASTM D1525 7 |
| -- | 138 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 15 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 15 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Edgewise |
| 7 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PP 1370 | Premix Oy | TPO | PRE-ELEC® |
| Multi-Flex® TPE A7321 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Evolue™ SP2510 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| HiFill® PA6/6 GF/M30 HS BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Lucofin® 1461 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |