MAJORIS DFR 907
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DdmE0q_MAJORIS-DFR-907.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DFR 907 is a halogen free flame retardant compound UL 94 VO (with Yellow card) , intended for injection moulding. The product is available in natural but other colours can be provided on request. DFR 907 is especially designed for technical parts. In addition to having good flame retardant properties this product has an extremely low level of toxicity in case of fire. DFR 907 is mainly intended for the injection moulding of electrical components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.5 - 2.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| -15°C, injection molding | 5100 | MPa | ISO 527-2 |
| 0°C, injection molding | 3700 | MPa | ISO 527-2 |
| 23°C, injection molding | 2800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield, -15°C, injection molding | 43.0 | MPa | ISO 527-2 |
| Yield, 0°C, injection molding | 36.0 | MPa | ISO 527-2 |
| Yield, 23°C, injection molding | 26.0 | MPa | ISO 527-2 |
| Fracture, -15°C, injection molding | 40.0 | MPa | ISO 527-2 |
| Fracture, 0°C, injection molding | 32.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, -15°C, injection molding | 3.6 | % | ISO 527-2 |
| Yield, 0°C, injection molding | 3.4 | % | ISO 527-2 |
| Yield, 23°C, injection molding | 2.7 | % | ISO 527-2 |
| Fracture, -15°C, injection molding | 5.0 | % | ISO 527-2 |
| Fracture, 0°C, injection molding | 9.0 | % | ISO 527-2 |
| Fracture, 23°C, injection molding | 8.0 | % | ISO 527-2 |
| Flexural Modulus 1(23°C, Injection Molded) | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180 | ||
| -15°C | 2.0 | kJ/m² | ISO 180 |
| 0°C | 2.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 99.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 50.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold-on Pressure: 50 - 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FP63E23 | The Matrixx Group, Inc. | Nylon 6 | Matrixx |
| polyvic® IM-1822-FT 31 | Unipack Plasindo | PVC, Unspecified | polyvic® |
| Escorene™ Ultra LD 706.15 Molding | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| KEBAFORM® C 2527 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Wanthane® WHT-1172IC | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |