Maxxam™ NR-818.H001-8086
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ddh9AH_Maxxam-NR-818-H001-8086.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Good heat stabilization |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.90 - 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 35.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2200 | MPa | ASTM D790 |
| Flexural Strength 3 | 50.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 75.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 200 - 240 | °C | |
| Middle Temperature | 200 - 240 | °C | |
| Front Temperature | 200 - 240 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fiberfil® J-68/30/E | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| LNP™ LUBRICOMP™ DCL32 compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |
| MAJORIS G401 - 7841/E | AD majoris | PP, Unspecified | MAJORIS |
| SQUARE® LSR1920-30AH/BH | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| ESTOPLAST XU 230BB01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |