LNP™ THERMOCOMP™ KF006 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DdI4MN_LNPTHERMOCOMPKF006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KF006 is a compound based on Acetal Copolymer resin containing Glass Fiber Also known as: LNP* THERMOCOMP* Compound KFX-1006 Product reorder name: KF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.62 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Flow | 0.50 - 0.80 | % | Internal method |
| Transverse flow | 0.80 - 1.1 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 125 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7400 | MPa | ISO 178 |
| Flexural Stress | 163 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 164 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 161 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MORETEC™ 0168H | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| NEFTEKHIM PP 8300L | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Ad-Tech Epoxy EC-410 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Kepital® TX-11H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| NORYL™ LS6010 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |