TORZEN® G3300L NC01
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DcoOEs_TORZENG3300LNC01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN® G3300L NC01 is a 33% glass reinforced, natural, PA66 resin suitable for many injection molding applications where high tensile strength and dimensional stability are needed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow : 2.00mm | 0.90 - 1.1 | % | ISO 294-4 |
| Flow : 2.00mm | 0.30 - 0.40 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.8 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 205 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.1 | % | ISO 527-2 |
| Flexural Modulus | 9500 | MPa | ISO 178 |
| Flexural Stress | 285 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 10 | kJ/m² | ISO 179 |
| 23°C | 12 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 248 | °C | ISO 75-2/A |
| Melting Temperature | 262 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.080 - 0.18 | % | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Back Pressure | 0.200 - 1.00 | MPa | |
| Cushion | 4.00 - 6.00 | mm | |
| Vent Depth | 7.0E-3 - 0.040 | mm | |
| Screw Speed | Low rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4005 SI | RTP Company | PPA | RTP |
| RTP 505 HB | RTP Company | SAN | RTP |
| Elastollan® B 85 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Hylon® N1213THL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| LUVOCOM® 1100-8166 | Lehmann & Voss & Co. | PESU | LUVOCOM® |