| Infino HN-3203G is a Polycarbonate (PC) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/10.0 kg | 11 | g/10 min | ASTM D1238 |
| 250°C/10.0 kg | 9.8 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Ash Content | 19 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4800 | MPa | ASTM D638 |
| -- | 5000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 110 | MPa | ASTM D638 |
| Yield | 101 | MPa | ISO 527-2/50 |
| Break 3 | 98.0 | MPa | ASTM D638 |
| Break | 101 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 4.1 | % | ASTM D638 |
| Break | 3.4 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 5400 | MPa | ASTM D790 |
| -- | 5300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 6 | 160 | MPa | ASTM D790 |
| -- | 137 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 160 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 120 | J/m | ASTM D256 |
| 23°C 8 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 145 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 140 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/B50 |
| -- | 152 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| 6.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 260 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Pressure | 93.2 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | Thickness: 4 mm |
| 8 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veroplas PA2002 | PlastxWorld Inc. | Nylon 6 | Veroplas |
| Andur 70 DP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Karina IVORY PVC COMPOUND -E MICRO-EX 6535/ 1-BZ (**) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ ECF62 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| MARPOL® Homo 7.0 | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |