Menzolit® BMC 3100
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dc0RgA_Menzolit-BMC-3100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® BMC 3100 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® BMC 3100 is a special BMC suitable for the use in head lamp reflectors. Because of its high temperature resistance and dimensional stability as well as low coefficient of thermal expansion, complex shapes and good reflective properties can be made. Because of its temperature resistance the precise geometry of the reflector will keep its precise shape even at high temperature. It has found specific use in the field of reflectors for automotive head lamps but its use as lamp housings for household and office lighting equipment is possible as well. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.00 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- | -0.030 | % | ISO 2577 |
| -- 1 | 0.0 | % | DIN 53464 |
| Water Absorption (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | 1.0 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 11000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 79.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.30 | Internal Method | |
| Matrix Crazing Strain | 0.30 | % | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 15 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
| Continuous Use Temperature | 190 | °C | Internal Method |
| Glass Transition Temperature | 185 | °C | DSC |
| CLTE - Flow | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (2.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 160 | °C | |
| Injection Pressure | 2.00 to 8.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-2090-70A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Generic PS (EPS) | Generic | PS (EPS) | Generic |
| LubriOne™ SF-30CF/15T BLACK | PolyOne Corporation | PPS | LubriOne™ |
| Sylvin 802-88 Green 3185 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9084-68 WHITE 1123 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |