Halene H P5200
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DbVQxR_Halene-H-P5200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
P5200 is a pipe grade HDPE, produced by the Mitsui CX Technology. This resin is recommended for PE 63 compliant pressure pipes. P5200 combines excellent processability with good creep resistance, ESCR and mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.80 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, Compression Molded | 25.0 | MPa | |
| Break, Compression Molded | 38.0 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, Compression Molded | 7.0 | % | |
| Break, Compression Molded | 750 | % | |
| Flexural Modulus (Compression Molded) | 900 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 180 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 67.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 3 |
| Oxidation Induction Time | > 30 | min | ASTM D3895 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 180 | °C | |
| Cylinder Zone 2 Temp. | 150 to 180 | °C | |
| Cylinder Zone 3 Temp. | 150 to 180 | °C | |
| Cylinder Zone 4 Temp. | 150 to 180 | °C | |
| Cylinder Zone 5 Temp. | 150 to 180 | °C | |
| Die Temperature | 170 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon T1910H-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| Thermylene® P4-30FG-0522 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Kepamid® 1825GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| KOPET® KP133G30BL | Kolon Plastics, Inc. | PET | KOPET® |
| Karina IVORY PVC COMPOUND 807D35/1-C-AC-HSF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |