MAJORIS FFR057 - 3717 Datasheet,PP, Unspecified,AD majoris-SHANGHAI SUSHENG

Message
FFR057 - 3717 is part of a new material family with low halogen no blooming flame retardant, high impact strength, high gloss and antistatic as well as an excellent UV-resistance and very low war page behaviour. Intended for injection moulding. The product is available in natural (FFR057) but other colours can be provided on request. APPLICATIONS FFR057 - 3717 is recommended for indoor or outdoor electrical and lighting applications like plugs, sockets, connectors, capacitor housings, small junction boxes or lamp covers; where chemical resistance, impact and flammability behaviours are required.

General Information
Additive	Antistatic Flame Retardant
Features	Antistatic Flame Retardant Good Chemical Resistance Good UV Resistance High Gloss High Impact Resistance Low Halogen Content Low Warpage Non-Blooming Recyclable Material
Uses	Connectors Electrical Housing Electrical/Electronic Applications Lighting Applications Outdoor Applications Plugs
Appearance	Colors Available Natural Color
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.965	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	18	g/10 min	ISO 1133
Spiral Flow ¹	102	cm
Molding Shrinkage
Across Flow	1.2	%
Flow : 2.00 mm	1.2	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1500	MPa	ISO 527-2
Tensile Stress
Yield	28.0	MPa	ISO 527-2/50
Break	12.0	MPa	ISO 527-2
Tensile Strain
Yield	6.0	%	ISO 527-2/50
Break	80	%	ISO 527-2
Flexural Modulus	1400	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-20°C	2.2	kJ/m²
23°C	5.5	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-20°C	71	kJ/m²
23°C	190	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	94.0	°C	ISO 75-2/B
Vicat Softening Temperature
--	154	°C	ISO 306/A
--	79.0	°C	ISO 306/B
Ball Pressure Test (125°C)	Pass		IEC 60335-1
RTI Elec	110	°C	UL 746
RTI Imp	115	°C	UL 746
RTI Str	115	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	7.8E+15	ohms	IEC 60093
Volume Resistivity	2.0E+16	ohms·cm	IEC 60093
Electric Strength	41	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
50 Hz	2.25
1 kHz	2.25
100 kHz	2.24
Dissipation Factor			IEC 60250
50 Hz	1.5E-3
1 kHz	1.5E-3
100 kHz	2.0E-3
Arc Resistance (3.00 mm)	PLC 5		ASTM D495
Comparative Tracking Index (CTI) (3.00 mm)	PLC 0		UL 746
Comparative Tracking Index			IEC 60112
--	> 600	V
Solution B	> 600	V
Needle Flame Test (1.00 mm)	Pass		IEC 60695-11-5
High Amp Arc Ignition (HAI)			UL 746
1.50 mm	PLC 0
3.00 mm	PLC 0
High Voltage Arc Tracking Rate (HVTR)			UL 746
1.50 mm	PLC 0
3.00 mm	PLC 0
Hot-wire Ignition (HWI)			UL 746
1.50 mm	PLC 3
3.00 mm	PLC 2

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm, All)	V-2		UL 94
Glow Wire Flammability Index			IEC 60695-2-12
0.500 mm	850	°C
3.00 mm	960	°C
Glow Wire Ignition Temperature (1.00 mm)	850	°C	IEC 60695-2-13
Oxygen Index	25	%	ISO 4589-2

Injection	Nominal Value	Unit
Processing (Melt) Temp	180 to 200	°C
Mold Temperature	20.0 to 50.0	°C

Note Message
1 .	Melt Temperature: 200°C

Category:	PP, Unspecified , Polypropylene
Manufacturer:	AD majoris
Trademark:	MAJORIS
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	DbGlOA_MAJORIS-FFR057---3717.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TEREZ PA 6 7600	TER HELL PLASTIC GMBH	Nylon 6	TEREZ PA 6
VALOX™ 7062 resin	SABIC Innovative Plastics Europe	PBT+PET	VALOX™
KOPLA PA6 KNG1050	KOPLA Co., Ltd.	Nylon 6	KOPLA PA6
SQUARE® LIM3919-30A/B	Shenzhen SQUARE Silicone Co., Ltd.	Silicone Rubber, LSR	SQUARE®
LNP™ LUBRICOMP™ OL004 compound	SABIC Innovative Plastics	PPS, Linear	LNP™ LUBRICOMP™