barex® 210 Injection Grade
| Category: | Nitrile Resin , Acrylonitrile Copolymer |
| Manufacturer: | INEOS Barex |
| Trademark: | barex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DaiMIY_barex-210-Injection-Grade.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Barex Injection Grade resin is an impact modified acrylonitrile-methyl acrylate copolymer with excellent gas barrier and a wide range of chemical resistance. It can easily be used in injection molding, injection blow molding, and injection stretch blow molding of high barrier containers and chemically resistant parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/21.6 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 96.5 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability (23°C, 100% RH) | 0.31 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate | 2.0 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 74.4 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 66.1 | °C | ASTM D648 |
| CLTE - Flow (20 to 80°C) | 6.7E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat (20°C) | 1340 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 254 µm) | 120 | ASTM D2457 | |
| Transmittance (254 µm) | 92.5 | % | ASTM D1003 |
| Haze (254 µm) | 2.7 | % | ASTM D1003 |
| Yellowness Index (0.254 mm) | 2.5 | YI | ASTM D1925 |
| Additional Information |
|---|
| Yield: 24080 in²-mil/lbMelt Index, ASTM D1238, 200°C/27.5 lbs: 12 g/10minWater Vapor Trans Rate, ASTM F1249, 100°F, 90% RH: 5 g-mil/100in²at-dNitrogen Permeability, ASTM D3985, 73°F, 100% RH: 0.2 cm³-mil/100 in²-24 hrs-atmCarbon Dioxide Permeability, ASTM D3985, 73°F, 100% RH: 1.2 cm³-mil/100 in²-24 hrs-atm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC7F-7015 | Spartech Polycom | PC | Spartech |
| Evoprene™ GC 5681 | AlphaGary | SEBS | Evoprene™ GC |
| INCOLOR PP BK002 | Infinity LTL Engineered Compounds | PP Homopolymer | INCOLOR |
| LNP™ LUBRICOMP™ KL003 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| KMI PP KM-503IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |