LNP™ LUBRICOMP™ KL004A compound
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Da4tr1_LNP-LUBRICOMP-KL004A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* KL004A is a compound based on Acetal Homopolymer resin containing 20% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* FULTON 404 D Product reorder name: KL004A |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 2.0 to 2.2 | % | |
| Across Flow : 24 hr | 2.0 to 2.2 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.23 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.37 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2550 | MPa | ASTM D638 |
| -- | 2700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 56.1 | MPa | ASTM D638 |
| Break | 50.6 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 11 | % | ASTM D638 |
| Break | 9.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2620 | MPa | ASTM D790 |
| -- | 2900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 86.0 | MPa | ASTM D790 |
| -- | 86.5 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.23 | ||
| vs. Itself - Static | 0.091 | ||
| Wear Factor - Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 560 | J/m | ASTM D4812 |
| 23°C 3 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.20 | J | ASTM D3763 |
| -- | 0.960 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 98.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BZM-23 BLK TL | Arkema | Nylon 11 | Rilsan® |
| RTP 384 TFE 15 | RTP Company | PC | RTP |
| SUPREME PP SP5665 | Supreme Petrochem Ltd. | PP, Unspecified | SUPREME PP |
| Hostacom BB 73 G YGYA Black | LyondellBasell Industries | PP Copolymer | Hostacom |
| Hyundai EP Breathable AT850/2102 | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Breathable |