Arlon® 49N
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Arlon-MED |
| Trademark: | Arlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DZvDcT_Arlon-49N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 49N is a low-flow epoxy prepreg engineered for bonding multilayer epoxy rigid-flex or attaching heatsinks to multilayer epoxy PCBs. With a high Tg, the prepreg can be used in high-performance or hightemperature applications compared to a standard difunctional epoxy low-flow. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792A |
| Water Absorption (24 hr) | 0.10 | % | Internal Method |
| Decomposition Temperature | Internal Method | ||
| 5% | 302 | °C | |
| Initial | 291 | °C |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength 1 | 1.6 | kN/m | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Expansion Rate (50 to 260°C) 2 | 3.1 | % | Internal Method |
| T260 | 10.0 | min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17900 | MPa | Internal Method |
| Flexural Strength | 234 | MPa | Internal Method |
| Poisson's Ratio 3 | 0.17 | ASTM D3039 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 170 | °C | Internal Method |
| CLTE - Flow | |||
| -- 4 | 1.4E-5 to 1.6E-5 | cm/cm/°C | Internal Method |
| < 170°C 5 | 8.7E-5 | cm/cm/°C | Internal Method |
| > 170°C 6 | 2.5E-4 | cm/cm/°C | Internal Method |
| Thermal Conductivity (100°C) | 0.25 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | Internal Method | ||
| -- 7 | 4.0E+12 | ohms | |
| -- 8 | 2.9E+13 | ohms | |
| Volume Resistivity | Internal Method | ||
| -- 9 | 3.3E+12 | ohms·cm | |
| -- 10 | 2.6E+13 | ohms·cm | |
| Dielectric Strength | 39 | kV/mm | Internal Method |
| Dielectric Constant (1 MHz) | 4.40 | Internal Method | |
| Dissipation Factor (1 MHz) | 0.025 | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | After Thermal Stress |
| 2 . | Z-axis |
| 3 . | x and y direction |
| 4 . | Y-axis |
| 5 . | Z-axis |
| 6 . | Z-axis |
| 7 . | E24/125 |
| 8 . | C96/35/90 |
| 9 . | E24/125 |
| 10 . | C96/35/90 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 17.NB | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| Rhelon G1833HR-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| TOTAL Polystyrene 260-75 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| ALTECH® PA66 A 1000/310 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Karina STRAW PVC COMPOUND 801-38/39-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |