LNP THERMOCOMP MX89510 is a compound based on Polypropylene resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-M-89510 Product reorder name: MX89510 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.02 | g/cm³ | |
| -- | 1.01 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.80 to 2.0 | % | |
| Across Flow : 24 hr | 0.90 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3830 | MPa | ASTM D638 |
| -- | 3540 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 52.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/5 |
| Break 3 | 52.0 | MPa | ASTM D638 |
| Break | 48.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2/5 |
| Break 5 | 3.4 | % | ASTM D638 |
| Break | 3.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2800 | MPa | ASTM D790 |
| -- 7 | 2960 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 76.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 21 | J/m | ASTM D256 |
| 23°C 9 | 2.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 370 | J/m | ASTM D4812 |
| 23°C 10 | 22 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 4.00 | J | ASTM D3763 |
| -- | 1.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 156 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 153 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 131 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 119 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vital-Line SHE5240A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| ACCUTECH™ HP0334G15M15CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Arnite® TV6 220 | DSM Engineering Plastics | PBT | Arnite® |
| ExxonMobil™ LLDPE LL 1004YB Wire & Cable | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| HiFill® PC/PBT IM 6702 | Techmer Engineered Solutions | PC+PBT | HiFill® |