Vyncolit® X7500
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DYKqUy_Vyncolit-X7500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit X7500 is a glass fibre reinforced phenolic moulding compound with superior mechanical properties: very high tensile and flexural strength combined with high elongation at break. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.17 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | 0.20 | % | ISO 62 |
| Post Shrinkage | 0.020 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.6 | % | ISO 178 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Type | PF 2 C3 | ||
| Pourability | Good |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2 |
| Flexural Modulus | 17500 | MPa | ISO 178 |
| Flexural Stress | 250 | MPa | ISO 178 |
| Compressive Stress | 280 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 21 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | °C | ISO 75-2/Af |
| CLTE | TMA | ||
| Flow | 2.0E-5 | cm/cm/°C | |
| Transverse | 3.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 7.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 4.0E+11 | ohms·cm | DIN 53482 |
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Insulation Resistance | IEC 60167 | ||
| -- 1 | 1.0E+11 | ohms | |
| -- 2 | 1.0E+12 | ohms |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-1 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Wet after 24 hr in water |
| 2 . | Dry |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-G20 | Polymer Resources Ltd. | Nylon 66 | PRL |
| Softell TKG 442N C12507 | LyondellBasell Industries | Polyolefin, Unspecified | Softell |
| Axiall PVC 12881 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Ferro PP LPP40BD43NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Sylvin 4280-80FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |