VALOX™ V9260CS resin
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DXgEA1_VALOX-V9260CS-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Color Stable Glass filled PET |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.20 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.80 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.27 | % | |
| Equilibrium, 23°C, 50% RH | 0.070 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 155 | MPa | |
| Break | 155 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 2.0 | % | |
| Break | 2.0 | % | |
| Flexural Modulus 1 | 9100 | MPa | ISO 178 |
| Flexural Stress | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength 3 | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 230 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 230 | °C | ISO 306/B50 |
| -- | 235 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 2.5E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 1.0E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 90.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RV350LW 333 NER 4815 | Radici Plastics | Nylon 66 | Radilon® |
| THERMOLAST® K TC7PAZ (Series: AD/PA) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Alcryn® 2180 BK | Advanced Polymer Alloys | MPR | Alcryn® |
| DIOSHY® HP-930NC | DIOSHY Co.,Ltd. | SEBS | DIOSHY® |
| Kepamid® 2325GFS | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |