DOWLEX™ SC 2107G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DXHZ6s_DOWLEX-SC-2107G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™SC 2107G is suitable for processing of high-speed production lines. The film prepared with DOWLEX SC 2107G polyethylene resin has excellent tensile properties, excellent tear strength and impact resistance, and excellent optical properties. Main features:
Application field:
Meet the requirements of the following regulations:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Tensile Strength 1 | ASTM D882 | ||
| MD : Yield, 23 µm | 6.30 | MPa | ASTM D882 |
| TD : Yield, 23 µm | 5.90 | MPa | ASTM D882 |
| MD : Break, 23 µm | 43.0 | MPa | ASTM D882 |
| TD : Break, 23 µm | 28.0 | MPa | ASTM D882 |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Break, 23 µm | 470 | % | ASTM D882 |
| TD : Break, 23 µm | 900 | % | ASTM D882 |
| Dart Drop Impact 3(23 µm) | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength 4 | ASTM D1922 | ||
| MD : 23 µm | 410 | g | ASTM D1922 |
| TD : 23 µm | 540 | g | ASTM D1922 |
| Film tensile properties-maximum stretch to penetration 5 | 130 | Internal method | |
| Film Tensile Properties-Maximum Elongation 6 | 240 | % | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 7(45°, 23.0 µm) | 92 | ASTM D2457 | |
| Haze 8(23.0 µm) | 0.70 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 280 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 熔体温度：220-280°C 冷却辊温度：20-60°C 脱离速度：150-450 米/分 建议的厚度范围：10-60 µm |
| Note Message | |
|---|---|
| 1 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 2 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 3 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 4 . | Method B; Cast film, 250 m/min; Cooling roller 25 c. |
| 5 . | Cast film, 250 m/min; Cooling roller 25°C; Measured on test bench; Maximum prestretching before penetration of sharp probe. |
| 6 . | Cast film, 250 m/min, cooling roller 25°C; Measured on the test bench. |
| 7 . | Cast film, 250 m/min; Cooling roller 25 c. |
| 8 . | Cast film, 250 m/min; Cooling roller 25 c. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silplus® 80 MP | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| Dynaglide® DW 611 | DeWAL Industries | PTFE | Dynaglide® |
| HiFill® PA6 GF50 L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Delrin® 525GR BK000 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| OPTODYNE™ UV-3200 | DAIKIN AMERICA, INC. | Epoxy | OPTODYNE™ |