Keyflex® BT 1163D
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Keyflex® BT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DXEvAF_Keyflex-BT-1163D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, Medium Modulus Application Cable & Wire Jackets, Hose & Tubing |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm, Injection Molded) | 1.1 to 1.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C, Injection Molded) | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm, Injection Molded | 16.7 | MPa | |
| Break, 23°C, 2.00 mm, Injection Molded | 37.3 | MPa | |
| Tensile Elongation 2(Break, 23°C, 2.00 mm, Injection Molded) | 700 | % | ASTM D638 |
| Flexural Modulus 3(23°C, 6.40 mm, Injection Molded) | 216 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4(23°C) | 160 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.40 mm, Injection Molded | 98 | J/m | |
| 23°C, 6.40 mm, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm, Injection Molded) | 110 | °C | ASTM D648 |
| Peak Melting Temperature | 208 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 26 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Nozzle Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Cylinder Zone 1 Temp. | 210 to 230 | °C | |
| Cylinder Zone 2 Temp. | 215 to 235 | °C | |
| Cylinder Zone 3 Temp. | 225 to 245 | °C | |
| Cylinder Zone 4 Temp. | 225 to 245 | °C | |
| Adapter Temperature | 225 to 245 | °C | |
| Melt Temperature | 210 to 240 | °C | |
| Die Temperature | 215 to 255 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solprene® 1322 | Dynasol Elastomers | SBR, Solution | Solprene® |
| APEX® 4157 | Teknor Apex Company | PVC, Flexible | APEX® |
| Generic PEEK - Nano, Carbon | Generic | PEEK | Generic |
| MAJ'ECO DG308BS - 8229 | AD majoris | Biodeg Polymers | MAJ'ECO |
| OTECH CPE OTE4535 - Power Jacket | OTECH Corporation | CPE | OTECH CPE |