Bergamid™ B700 UF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DW0gSc_Bergamid-B700-UF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bergamid™ B700 UF is a Polyamide 6 (Nylon 6) product. It is available in Africa & Middle East, Asia Pacific, or Europe. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.18 | g/cm³ | DIN 53479 |
| K-Value 2 | 74.0 to 78.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 20 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.3 | kJ/m² | |
| 23°C | 8.4 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 190 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Maximum Use Temperature | IEC 60216 | ||
| -- 3 | 85 | °C | |
| Short Time | 160 | °C | |
| Melting Temperature (DSC) | 223 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 45 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 7.00 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm, ALL) | V-0 | Internal Method | |
| Glow Wire Ignition Temperature 4(3.00 mm) | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | ±0.03 g/cm³ |
| 2 . | 96% H2SO4 |
| 3 . | Continuous (GTP 50% Tensile) |
| 4 . | 0.8 mm wire |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® TXE95 | A. Schulman Europe | ABS | RONFALIN® |
| Unichem 5790 | Colorite Polymers | PVC, Unspecified | Unichem |
| Arlon® 1287 LI | Greene, Tweed & Co. | PEEK | Arlon® |
| NOVAPOL® HB-W646-UH | NOVA Chemicals | HDPE | NOVAPOL® |
| LNP™ VERTON™ MV008S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |