RTP 1303 TFE 20
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DVtKdC_RTP-1303-TFE-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber Reinforced - PTFE Lubricated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 | % | ASTM D955 |
| Moisture Content | 0.040 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9650 | MPa | ASTM D638 |
| Tensile Strength | 103 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 to 2.0 | % | ASTM D638 |
| Flexural Modulus | 9310 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 307 to 329 | °C | |
| Mold Temperature | 135 to 177 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx F662E33 | The Matrixx Group, Inc. | Nylon 66 | Matrixx |
| TECHNYL® B 238 BLACK 21 N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |
| LNP™ THERMOCOMP™ 9X02540 compound | SABIC Innovative Plastics | PC+PET | LNP™ THERMOCOMP™ |
| OP - PC - Unfilled 912 | Oxford Polymers | PC | OP - PC - Unfilled |
| Osterlene® PPC-20-NB | Osterman & Company | PP Impact Copolymer | Osterlene® |