Razamid® B111 GR35
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Razin™ Engineering Plastics |
| Trademark: | Razamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DV3w8z_Razamid-B111-GR35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Razamid B111 GR35 is an injection grade natural color polyamide 6 resin reinforced with 35% Glass Fiber. It combines good strength, stiffness and toughness as well as excellent heat, chemical and abrasion resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 195 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 10500 | MPa | ASTM D790 |
| Flexural Strength | 280 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 18.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 220 | °C | |
| 1.8 MPa, Unannealed | 212 | °C | |
| Vicat Softening Temperature | 210 | °C | ASTM D1525 |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.80 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 55.0 to 140 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nycal™ 2120H Bk-7 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| Chiao Fu PA66 MD212STG33 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Hostacom M2 U02 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Karina WHITE PVC COMPOUND 807-10/236-H-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Edistir® N 3560 | Versalis S.p.A. | PS (GPPS) | Edistir® |