Akulon® K222-KGV6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DTUdVL_Akulon-K222-KGV6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® K222-KGV6 is a Polyamide 6 (Nylon 6) material filled with 30% glass fiber. It is available in Asia Pacific or Europe. Important attributes of Akulon® K222-KGV6 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.55 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 5.6 | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.6 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 43 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 180 | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 525 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | |
| 1.60 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 725 | °C | |
| 1.60 mm | 725 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 225 to 235 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 235 to 250 | °C | |
| Nozzle Temperature | 235 to 255 | °C | |
| Processing (Melt) Temp | 245 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1202-65D | RTP Company | TPU, Unspecified | RTP |
| SMOKEGUARD™ III 1091-A1 NATURAL | AlphaGary | PVC, Unspecified | SMOKEGUARD™ III |
| HiFill® PEEK GF30 A HR 102 | Techmer Engineered Solutions | PEEK | HiFill® |
| Karina WHITE PVC 837-10/ 55-AY-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ DE0029 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |