POLYLAN AG10AP
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | POLYMA Kunststoff GmbH & Co. KG |
| Trademark: | POLYLAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DS7WDt_POLYLAN-AG10AP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYLAN AG10AP is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by extrusion and is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/10.0 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 96 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1960 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield, 23°C) | 34.0 | MPa | ASTM D638, ISO 527-2 |
| Flexural Strength (23°C) | 57.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 410 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 85.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 12.7 mm | 97.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/A, ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V961 BLK580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Silamid® CV20 | Roonamid a.s. | Nylon 6 | Silamid® |
| Torelina® A673M | Toray Resin Company | PPS | Torelina® |
| AKROMID® A3 GF 13 S3 black (3768) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Karina WHITE PVC COMPOUND -E 898-10/161-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |