Category: | Nylon 6 , Polyamide 6 |
Manufacturer: | UBE Engineering Plastics, S.A. |
Trademark: | UBE Nylon |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | DQugKl_UBE-Nylon-1015-UC2.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
UBE NYLON 1015 UC2 is special modified, heat stabilized Polyamide 6. The material is a so called Nylon Clay Hybrid. It contents exfoliated, by polymerization process incorporated silicate platelets. |
General Information | |
---|---|
Filler / Reinforcement |
|
Additive |
|
Features |
|
Appearance |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Yield) | 96.0 | MPa | ASTM D638 |
Tensile Elongation (Break) | 50 | % | ASTM D638 |
Flexural Modulus | 3500 | MPa | ASTM D790 |
Flexural Strength | 138 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 47 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, not annealed | 197 | °C | ASTM D648 |
1.8 MPa, not annealed | 140 | °C | ASTM D648 |
Melting Temperature | 220 | °C | DSC |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
Additional Information |
---|
Specific Modulus: 3300 MPa |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Sanren M800E (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
Veradel® 3250 | Solvay Specialty Polymers | PESU | Veradel® |
VisiJet® M3 Crystal | 3D Systems | Unspecified | VisiJet® |
Elastocon® SMR1450 | Elastocon TPE Technologies | TPO (POE) | Elastocon® |
Lucky Enpla LMA1003 | Lucky Enpla Co LTD | Acrylic (PMMA) | Lucky Enpla |