NORYL™ NH5020 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DQgZDX_NORYLNH5020resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrene resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame retardant. The material is suitable for injection molding and is available in custom colors. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 9.8 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 10.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.25 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2730 | MPa | ASTM D638 |
| -- | 3060 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 79.2 | MPa | ASTM D638 |
| Yield | 80.1 | MPa | ISO 527-2/50 |
| Fracture 3 | 62.2 | MPa | ASTM D638 |
| Fracture | 77.5 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 4.8 | % | ISO 527-2/50 |
| Fracture 5 | 15 | % | ASTM D638 |
| Fracture | 5.7 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3000 | MPa | ASTM D790 |
| -- 7 | 2980 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 126 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 122 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 7.9 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 59 | J/m | ASTM D256 |
| 23°C | 91 | J/m | ASTM D256 |
| -30°C 10 | 6.1 | kJ/m² | ISO 180/1A |
| 23°C 11 | 8.1 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 19.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 122 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm | 134 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 117 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 123 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 119 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 138 | °C | ASTM D1525, ISO 306/B50 11 13 |
| -- | 139 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 49 | kV/mm | IEC 60243-1 |
| Arc Resistance 14 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 2.00 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Resistance to Ignition (HVAR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-2 | UL 94 | |
| 0.750 mm | V-0 | UL 94 | |
| 2.50 mm | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 243 - 293 | °C | |
| Middle Temperature | 254 - 299 | °C | |
| Front Temperature | 266 - 304 | °C | |
| Nozzle Temperature | 277 - 304 | °C | |
| Processing (Melt) Temp | 277 - 304 | °C | |
| Mold Temperature | 71.1 - 98.9 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| 14 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREX TA 2351 HD | SILON s.ro | TP, Unspecified | TABOREX |
| Moplen Z11G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Texin® 260 | Covestro - PUR | TPU-Polyester | Texin® |
| Next Nylon 6 Prime Series NG30-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Bayblend® M750 | Covestro - Polycarbonates | PC+ABS | Bayblend® |