CALIBRE™ 502-3
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DQGwMf_CALIBRE-502-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 502-3 TC0302156 Resin is specially designed to provide increased fatigue resistance for extruded solid sheets. The resin is UV bulk stabilized, but outdoor use requires a co-extruded UV cap layer. It is recommended to apply in that case a 40 to 50 micron co-extruded layer of CALIBRE™ 320UV. CALIBRE 502-3 TC0302156 is also suitable to extrude corrugated solid sheet thanks to its low melt sagging. Main Characteristics
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm, Injection Molded) | 2200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield, 4.00 mm, Injection Molded | 61.0 | MPa | |
| Break, 4.00 mm, Injection Molded | 68.0 | MPa | |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield, 4.00 mm, Injection Molded | 6.0 | % | |
| Break, 4.00 mm, Injection Molded | 100 | % | |
| Flexural Modulus (4.00 mm, Injection Molded) | 2300 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| 4.00 mm, Injection Molded | 90.3 | MPa | ASTM D790 |
| 4.00 mm, Injection Molded | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 72 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 4.00 mm, Injection Molded) | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 145 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 132 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 158 | °C | ISO 306/B50, ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 2(1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ RXD110 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| Ultramid® 66 H2 G/35-V0KB1 BK3324 | BASF Corporation | Nylon 66 | Ultramid® |
| Ultramid® B3ZG8 BK20560 | BASF Corporation | Nylon 6 | Ultramid® |
| GERMAFORM 9 TF | Kunststoff-Kontor-Hamburg GmbH | Acetal (POM) Copolymer | GERMAFORM |
| Epoxies, Ect. 20-2370 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |