Taizhou Phenolic PF2A4-151J
| Category: | Phenolic , Phenolic |
| Manufacturer: | Taizhou Changxiong Plastic Co., Ltd. |
| Trademark: | Taizhou Phenolic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DPzTBG_Taizhou-Phenolic-PF2A4-151J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taizhou Phenolic PF2A4-151J is a phenolic (Phenolic) material,. This product is available in the Asia-Pacific region and is processed by injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | < 1.45 | g/cm³ | Internal method |
| Molding Shrinkage | 0.60 - 0.90 | % | ISO 2577 |
| Water Absorption | mg | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Stress | > 85.0 | MPa | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | > 1.7 | kJ/m² | Internal method |
| Charpy Unnotched Impact Strength | > 4.5 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 170 | °C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+11 | ohms | Internal method |
| Volume Resistivity | > 1.0E+12 | ohms·cm | Internal method |
| Dielectric Strength | > 10 | kV/mm | Internal method |
| Dissipation Factor | < 0.050 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 70.0 - 80.0 | °C | |
| Front Temperature | 90.0 - 100 | °C | |
| Mold Temperature | 165 - 180 | °C | |
| Injection Pressure | 80.0 - 160 | MPa | |
| Back Pressure | 1.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Curing Time: 10 to 20 s/mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1005 FR A UV | RTP Company | PBT | RTP |
| Moplen S60D | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Nipol® IR 2200 | Zeon Corporation | IR | Nipol® IR |
| Hifax CA 1110 G2 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Karina GRAY PVC COMPOUND 853-18/233-DY-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |