Ultramid® B3L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DPgOgP_Ultramid-B3L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3L is an impact-modified, easy flowing injection molding PA6 grade for fast processing. Applications Typical applications include impact-resistant articles such as housings, fittings, small parts and anchors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.10 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 100 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 1.1 | -- | % | |
| Water Absorption | ||||
| Saturation | 9.0 | -- | % | ASTM D570 |
| Saturation, 23°C | 9.0 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.5 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | 900 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Yield, 23°C | 69.0 | -- | MPa | ASTM D638 |
| Yield, 23°C | 70.0 | 35.0 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Yield, 23°C | 4.0 | -- | % | ASTM D638 |
| Yield, 23°C | 4.0 | 18 | % | ISO 527-2 |
| Break, 23°C | 25 | -- | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 25 | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 2500 | -- | MPa | ASTM D790 |
| 23°C | 2300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 10 kJ/m² | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact | ||||
| -40°C | 53 | -- | J/m | ASTM D256 |
| 23°C | 130 | -- | J/m | ASTM D256 |
| 23°C | 15 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 160 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 66.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | ||||
| -- | 4.0E-5 | -- | cm/cm/°C | ASTM E831 |
| -- | 8.5E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.400 mm | 65.0 | -- | °C | |
| 0.800 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.400 mm | 65.0 | -- | °C | |
| 0.800 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.400 mm | 65.0 | -- | °C | |
| 0.800 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | 1.0E+13 | 1.0E+10 | ohms·cm | ASTM D257 |
| -- | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant | IEC 60250 | |||
| 100 Hz | 4.00 | -- | ||
| 1 MHz | 3.50 | 6.40 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.010 | -- | ||
| 1 MHz | 0.024 | 0.24 | ||
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm | HB | -- | ||
| 0.800 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 285 | °C | |
| Mold Temperature | 65.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MFE® -W3 | Huachang Polymer Co., Ltd. | Vinyl Ester | MFE® |
| Tenite™ Butyrate 285A2R30016 Natural, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Tenite™ Acetate 132E5243225 Clear, Trsp | Eastman Chemical Company | CA | Tenite™ Acetate |
| KYDEX® XD | SEKISUI Polymer Innovations, LLC | PMMA+PVC | KYDEX® |
| Sylvin 9077-70 Blue 8401 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |