Vu-Stat™ Y-20
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Cyro LLC |
| Trademark: | Vu-Stat™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DOEEws_Vu-Stat-Y-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vu-Stat Y-20 compound is a transparent, electro-static dissipative acrylic-based multipolymer mainly for molding medical applications. Typical properties of of Vu-Stat Y-20 compound are:
Application: Used for drug delivery devices, inhalation devices, electronic packaging and any application where anti-static protection is required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Apparent Density | 0.65 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium) | < 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 54 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2140 | MPa | ASTM D638 |
| Tensile Strength | 39.3 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 18 | % | |
| Flexural Modulus | 1650 | MPa | ASTM D790 |
| Flexural Strength | 57.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C, 6.35 mm | 27 | J/m | |
| 23°C, 6.35 mm | 69 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm) | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 |
| CLTE - Flow (0 to 100°C) | 9.5E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3200 µm) | 85.0 | % | ASTM D1003 |
| Haze (3200 µm) | 7.0 | % | ASTM D1003 |
| Yellowness Index (3.20 mm) | -0.30 | YI | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BCC Resins BC 6004 | BCC Products Inc. | Epoxy | BCC Resins |
| Hostacom BJ44A | LyondellBasell Industries | PP Copolymer | Hostacom |
| KOPLA PA66 KDX1067 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Karina RED PVC COMPOUND 701D42/266-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Osterlene® PPH35NA | Osterman & Company | PP Homopolymer | Osterlene® |