Infino XP-2130A
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DNI0EO_Infino-XP-2130A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino XP-2130A is a Polyphenylene Sulfide (PPS) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (316°C/5.0 kg) | 120 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.30 to 1.2 | % | |
| Across Flow : 3.20 mm | 0.30 to 1.2 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Ash Content | |||
| -- | 30 | % | ASTM D5630 |
| -- | 30 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 120 | ASTM D785 | |
| R-Scale | 116 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5900 | MPa | ASTM D638 |
| 5.00 mm | 8000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield 2 | 140 | MPa | ASTM D638 |
| Yield | 128 | MPa | ISO 527-2/5 |
| Break 3 | 130 | MPa | ASTM D638 |
| Break, 5.00 mm | 115 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break 4 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 5 | |||
| -- | 9800 | MPa | ASTM D790 |
| -- | 10000 | MPa | ISO 178 |
| Flexural Strength 6 | |||
| -- | 200 | MPa | ASTM D790 |
| -- | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 88 79 | J/m | ASTM D256 |
| 23°C 8 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 282 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 289 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 275 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 275 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 280 to 290 | °C | |
| Middle Temperature | 290 to 300 | °C | |
| Front Temperature | 310 to 320 | °C | |
| Nozzle Temperature | 320 | °C | |
| Mold Temperature | 120 to 150 | °C | |
| Injection Pressure | 49.0 to 127 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | Thickness: 4 mm |
| 8 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 387 HF | RTP Company | PC | RTP |
| Fainplast PVC KL 94 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Fainplast PVC FKA 97 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Karina BLUE COLOR CONCENTRATE 06/830-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Softell TKG 300N 1 C12546 | LyondellBasell Industries | PP Copolymer | Softell |