RTP 203 A FR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DLXNaG_RTP-203-A-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - Flame Retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.4 | % | ASTM D570 |
| Moisture Content | 0.20 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8620 | MPa | ASTM D638 |
| Tensile Strength | 110 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 590 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 204 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 188 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.015 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ** Values per RTP Company testing. | V-0 | UL 94 | |
| 3.00 mm, ** Values per RTP Company testing. | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 243 - 279 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene XSene® HDPE XRC20 Blue | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Caltex PP H540 | GS Caltex | PP Homopolymer | Caltex PP |
| Expandable PS F22B | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Hanwha Total PP BI451 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Lucent PP TPP-320 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |