MEGOLON™ S380
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | AlphaGary |
| Trademark: | MEGOLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DIHayG_MEGOLON-S380.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MEGOLON® S380 is a thermoplastic, halogen free, fire retardant cable sheathing compound developed to meet the requirements of UK specification BS 7655 : 6.1 types LTS 1, 2, 3 & 4. APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 3.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| -- 1 | 12.6 | MPa | IEC 60811-1-2 |
| -- | 14.0 | MPa | IEC 60811-1-1 |
| Tensile Strain | |||
| Break 2 | 140 | % | IEC 60811-1-2 |
| Break | 180 | % | IEC 60811-1-1 |
| Elongation at Break | |||
| after 4 hours, in IRM 902 Oil : 70°C | 230 | % | |
| after 4 hours, in SAE 20 Oil : 70°C | 160 | % | |
| after 7 days, in IRM 902 Oil : 23°C | 190 | % | |
| after 7 days, in IRM 903 Oil : 23°C | 200 | % | |
| Tensile Strength | |||
| after 4 hours, in IRM 902 Oil : 70°C | 12.5 | MPa | |
| after 4 hours, in SAE 20 Oil : 70°C | 11.2 | MPa | |
| after 7 days, in IRM 902 Oil : 23°C | 13.9 | MPa | |
| after 7 days, in IRM 903 Oil : 23°C | 12.2 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Pressure Test (90°C) | 20 | % | IEC 60811-3-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Draw Down | 1.5:1.0 | ||
| Extruder Screw Compression Ratio | 1.0:1.0 to 2.0:1.0 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | |||
| -- | 9.30 | kN/m | BS 6469 99.1 |
| 23°C | 9.30 | kN/m | |
| 40°C | 7.70 | kN/m | |
| 50°C | 6.30 | kN/m | |
| 60°C | 5.20 | kN/m | |
| 70°C | 3.00 | kN/m |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 168 hr) | -10 | % | |
| Change in Tensile Strain at Break in Air (100°C, 168 hr) | -20 | % | |
| Change in Tensile Stress | |||
| 23°C, 168 hr, in IRM 902 Oil | -1.0 | % | |
| 23°C, 168 hr, in IRM 903 Oil | -13 | % | |
| 70°C, 4 hr, in IRM 902 Oil | -11 | % | |
| 70°C, 4 hr, in SAE 20 Oil | -20 | % | |
| 70°C, 168 hr, in Water | -10 | % | BS 6469 99.1 |
| Change in Tensile Strain at Break | |||
| 23°C, 168 hr, in IRM 902 Oil | 7.0 | % | |
| 23°C, 168 hr, in IRM 903 Oil | 11 | % | |
| 70°C, 4 hr, in IRM 902 Oil | 26 | % | |
| 70°C, 4 hr, in SAE 20 Oil | -11 | % | |
| 70°C, 168 hr, in Water | -10 | % | BS 6469 99.1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 35 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 140 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 150 | °C | |
| Cylinder Zone 5 Temp. | 160 | °C | |
| Melt Temperature | 165 to 175 | °C | |
| Die Temperature | 165 | °C |
| Note Message | |
|---|---|
| 1 . | after 7 days at 100°C |
| 2 . | after 7 days at 100°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Alpha PVC 3032-95 CLEAR 0003 | AlphaGary | PVC, Flexible | Alpha PVC |
| Geon™ Vinyl Wire & Cable WR7400L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| EPIMIX PBT GV0 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |
| HiFill® PA6 GB15 L BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Karina BLACK PVC COMPOUND -E TR-600-SA-48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |