NOVADURAN® 5010G45
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | NOVADURAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DIFrVP_NOVADURAN-5010G45.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NOVADURAN® 5010G45 is a Polybutylene Terephthalate (PBT) material filled with 45% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of NOVADURAN® 5010G45: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 2.00 mm | 0.90 | % | |
| Flow : 2.00 mm | 0.40 | % | |
| Water Absorption (Saturation, 23°C) | 0.060 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 165 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 14500 | MPa | ISO 178 |
| Flexural Stress | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 209 | °C | ISO 75-2/A |
| Melting Temperature | 224 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : -30 to 50°C | 3.0E-5 | cm/cm/°C | |
| Flow : -30 to 120°C | 3.0E-5 | cm/cm/°C | |
| Flow : 50 to 120°C | 3.0E-5 | cm/cm/°C | |
| Transverse : -30 to 50°C | 4.0E-5 | cm/cm/°C | |
| Transverse : -30 to 120°C | 5.0E-5 | cm/cm/°C | |
| Transverse : 50 to 120°C | 6.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 28 | kV/mm | |
| 2.00 mm | 25 | kV/mm | |
| Relative Permittivity (1 MHz) | 3.40 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.016 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 240 | °C | |
| Middle Temperature | 245 | °C | |
| Front Temperature | 255 | °C | |
| Nozzle Temperature | 255 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Screw Speed | 80 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 127 MF | RTP Company | PP Homopolymer | RTP |
| Spartech Polycom SCR7F-7010AU | Spartech Polycom | PC | Spartech |
| YUCLAIR® PI500 | SK Global Chemical | MDPE | YUCLAIR® |
| Fainplast PVC PG 86/AF | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| LNP™ THERMOCOMP™ JF006 compound | SABIC Innovative Plastics Europe | PESU | LNP™ THERMOCOMP™ |