| PA 6, non-reinforced, injection molding |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.14 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.14 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 3.00mm 1 | 0.96 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 3.00mm 2 | 0.20 | -- | % | ISO 2577 |
| Flow direction : 280°C, 3.00mm 3 | 0.90 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 3.00mm 4 | 0.21 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 10 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 150 | 50.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 3100 | 1000 | MPa | ASTM D638 |
| 23°C | 3200 | 900 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Yield, 23°C | 84.8 | 40.0 | MPa | ASTM D638 |
| Yield, 23°C | 85.0 | 40.0 | MPa | ISO 527-2/50 |
| Fracture, 23°C | 55.2 | 55.2 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Yield, 23°C | 4.0 | 25 | % | ASTM D638, ISO 527-2/50 |
| Fracture, 23°C | > 50 | > 50 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 20 | > 50 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 700 | MPa | ISO 899-1 |
| 1000 hr | -- | 570 | MPa | ISO 899-1 |
| Flexural Modulus | ||||
| 23°C | 2700 | 703 | MPa | ASTM D790 |
| 23°C 6 | 2800 | 800 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 5.0% strain, 23°C | 115 | 35.0 | MPa | ASTM D790 |
| 3.5% strain, 23°C | 95.0 | 25.0 | MPa | ISO 178/A |
| 23°C 7 | 115 | 35.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 8(23°C) | 6.0 | 9.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 9(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GR, 22-030 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ||||
| 23°C, 3.18 mm | 69 | 960 | J/m | ASTM D256 |
| -40°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | No Break | No Break | ISO 180/1U | |
| 23°C | No Break | No Break | ISO 180/1U | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 160 | -- | J | ISO 6603-2 |
| 23°C | 160 | 165 | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, unannealed, 39.9mm | 180 | -- | °C | ASTM D648 |
| 0.45 MPa, not annealed | 150 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | -- | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 3.99mm | 60.0 | -- | °C | ASTM D648 |
| 8.0 MPa, not annealed | 45.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 10 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec (1.50 mm) | 105 | -- | °C | UL 746 |
| RTI Imp (1.50 mm) | 65.0 | -- | °C | UL 746 |
| RTI (1.50 mm) | 75.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 - 1.0E+14 | 1.0E+12 - 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+11 - 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | |||
| 23°C, 1.00 mm | 30 | 35 | kV/mm | IEC 60243-1 |
| 23°C, 3.00 mm | 30 | 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 23°C, 50 Hz 11 | 3.80 | 16.0 | IEC 60250 | |
| 23°C, 1 MHz 12 | 3.40 | 4.70 | IEC 60250 | |
| 23°C, 100 Hz | 4.00 | 20.0 | IEC 60250 | |
| 23°C, 1 MHz | 3.50 | 4.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 0.050 | 2.8 | IEC 60250 | |
| 23°C, 100 Hz | 0.012 | 0.19 | IEC 60250 | |
| 23°C, 1 MHz | 0.060 0.020 | 0.40 0.14 | IEC 60250 | |
| Comparative Tracking Index | ||||
| Solution a | 600 | -- | V | IEC 60112 |
| Solution B | 600 | -- | V | IEC 60112 |
| -- | -- | 600 | V | ASTM D3638 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | UL 94 | |
| 1.50 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 | |
| 3.00 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 13 | 24 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 500 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 500 bar |
| 4 . | 150x105x3mm |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2 mm/min |
| 9 . | US-FMVSS302 |
| 10 . | 10°C/min |
| 11 . | Tinfoil Electrodes |
| 12 . | Tinfoil Electrodes |
| 13 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 7051 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| VENELENE® 11F1 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| Network Polymers PP PPB 25 2002 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| LOXIM 820 12 HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |
| TechnoDur PBT4 Natural (9999) | TechnoCompound GmbH | PBT | TechnoDur |