NORYL™ RN0206 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DGPKLN_NORYL-RN0206-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RN0206 is an unfilled Post Consumer Recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 10% PCR styrenic series resin content. Available in black only. |
| General Information | |
|---|---|
| Recycled Content |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 73.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 14 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 2500 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 100 mm Span) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 118 | °C | ASTM D648 |
| Ball Pressure Test 5(120°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Air) | 27 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 243 to 293 | °C | |
| Middle Temperature | 254 to 299 | °C | |
| Front Temperature | 266 to 304 | °C | |
| Nozzle Temperature | 277 to 304 | °C | |
| Processing (Melt) Temp | 277 to 304 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® FC 22 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Cereplast Compostables® 1006 | Cereplast, Inc. | PLA | Cereplast Compostables® |
| Elvax® 760 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Karina CLEAR PVC COMPOUND 57/200-D-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 65/XCF/40 | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |