SCLAIR® 99L
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DGGBDm_SCLAIR-99L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SCLAIR®99L is a high density polyethylene material,. This product is available in North America,. SCLAIR®The main features of 99L are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.962 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.55 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 | ASTM D2240 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 830 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 1330 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 27.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 22.0 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 39.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 22.0 | MPa | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 5 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 78 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2.5:1 to 4:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8627-45 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| BJB Polyurethane SP-82 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Electrafil® J-4/25/CF/15 NAT | Techmer Engineered Solutions | Nylon 612 | Electrafil® |
| Hylex® P1010L | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| Karina IVORY PVC COMPOUND 850-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |