SMOKEGUARD™ IV 1320 NATURAL
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | AlphaGary |
| Trademark: | SMOKEGUARD™ IV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DG6gx7_SMOKEGUARD-IV-1320-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A HIGH PERFORMANCE, 60°C RATED, LEAD FREE, LOW SMOKE PVC COMPOUND DESIGNED FOR DEMANDING APPLICATIONS WHERE PVDF WOULD TYPICALLY BE USED. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 - 1.74 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 69 - 75 | ASTM D2240 | |
| Shaw D, 15 seconds | 58 - 64 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D412 | ||
| 0.381 mm | 18.6 | MPa | ASTM D412 |
| 1.91 mm | 16.5 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Fracture, 1.91mm | 210 | % | ASTM D412 |
| Fracture, 0.381mm | 190 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 1(100°C, 168 hr) | -20 | % | UL Unspecified |
| Change in Ultimate Elongation in Air 2(100°C, 168 hr) | -29 | % | UL Unspecified |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -9.00 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (23°C, 100 MHz) | 3.40 | ASTM D150 | |
| Dissipation Factor (23°C, 100 MHz) | 0.014 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 57 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 166 | °C | |
| Cylinder Zone 3 Temp. | 171 | °C | |
| Cylinder Zone 4 Temp. | 174 | °C | |
| Cylinder Zone 5 Temp. | 174 | °C | |
| Adapter Temperature | 177 | °C | |
| Melt Temperature | 182 - 188 | °C | |
| Die Temperature | 177 | °C | |
| Extruder Screw Compression Ratio | 3.0:1.0 |
| Extrusion instructions |
|---|
| Melt temperature is critical, at elevated temperatures foaming may occur. It may be necessary to adjust barrel temp to attain the desired melt temp. Material should be dried prior to use |
| Note Message | |
|---|---|
| 1 . | Thickness: 15 mil |
| 2 . | Thickness: 15 mil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SNOLEN® EF 0.21/46 HT | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| SUMIPEX® HT01X | Sumitomo Chemical Co., Ltd. | Acrylic (PMMA) | SUMIPEX® |
| KOCETAL® WR701LOBE | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Indothene LL 20FS020 | Reliance Industries Limited | LLDPE | Indothene LL |
| Durethan® DP AKV 30 FN00 000000 | LANXESS GmbH | Nylon 66 | Durethan® |