Loyblend® TA-1100
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Loyblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DFYP0u_Loyblend-TA-1100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Loyblend® TA-1100 is a general purpose PC/ABS polymer alloy. This grade offers good impact resistance, good processability, high rigidity, high heat resistance, good dimensional stability and good color stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 260°C/2.16 kg | 10 | g/10 min | |
| 260°C/5.0 kg | 20 | g/10 min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2520 | MPa | ASTM D638 |
| Tensile Strength | 54.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 2420 | MPa | ASTM D790 |
| Flexural Strength | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 570 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 4.00 mm | 120 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | 103 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 210 to 245 | °C | |
| Middle Temperature | 220 to 250 | °C | |
| Front Temperature | 225 to 260 | °C | |
| Nozzle Temperature | 230 to 260 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Phenolic FM 1132P | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| Chemical Resources PET08512 | Chemical Resources, Inc. | PET | Chemical Resources |
| Fainplast PVC MPH 64 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Gallonprene® GP410-5501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| INEOS PP R08S-00 | INEOS Olefins & Polymers USA | PP Random Copolymer | INEOS PP |