Vipel® F701-S Series resins are high molecular weight, two-stage isophthalic, unsaturated polyester resin with the wet out, cure and handling characteristics of general purpose resins. The main feature is lower styrene content. They have an excellent shelf life and are ideal for filament winding and spray-up. A few selected resins are listed below. BENEFITS Corrosion resistance AOC's Vipel® F701-S series resins provide excellent corrosion resistance when used in contact with inorganic and organic acids. Solvent resistance is field-proven for many petroleum products such as kerosene, heating oil and crude oils. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. F701-S series resins contain less styrene than standard versions. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up and filament winding. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Styrene Content | 42 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Gel to Peak | 13.0 | min | |
| Peak Exotherm | 193 | °C | |
| Thixotropic Index 1 | 2.10 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 46 | ISO 75-2/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3860 | MPa | ISO 527-2 |
| Tensile Stress | 88.3 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.1 | % | ISO 527-2 |
| Flexural Modulus | 4210 | MPa | ISO 178 |
| Flexural Stress | 159 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 128 | °C | ISO 75-2/A |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density | 1.07 | g/cm³ | |
| Viscosity (25°C, Brookfield RVT) | 0.55 | Pa·s | |
| Gel Time (25°C) | 30 | min |
| Note Message | |
|---|---|
| 1 . | 2/20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® T100MK | Reliance Industries Limited | PP, Unspecified | REPOL® |
| Spartech Polycom 2850-60 | Spartech Polycom | PVC, Unspecified | Spartech |
| Vydyne® 50BW | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Nipol® LX435 | Zeon Corporation | Latex | Nipol® |
| Versaflex™ GP 2810-80N | PolyOne Corporation | TPE | Versaflex™ |