DECAL® 5431
| Category: | Phenolic , Phenolic |
| Manufacturer: | Synres-Almoco BV |
| Trademark: | DECAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DEaGVu_DECAL-5431.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Organically and inorganically filled phenolic moulding compound This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 to 1.45 | g/cm³ | ISO 1183 |
| Apparent Density | 0.55 to 0.70 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.60 to 0.80 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 1.5 | % | ISO 62 |
| Post Shrinkage 2 | 0.40 to 0.60 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| Compression Molded | 3000 to 5000 | MPa | |
| Injection Molded | 4000 to 6000 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Compression Molded | 50.0 to 70.0 | MPa | |
| Injection Molded | 50.0 to 70.0 | MPa | |
| Flexural Modulus | ISO 178 | ||
| Compression Molded | 6000 to 8000 | MPa | |
| Injection Molded | 6000 to 8000 | MPa | |
| Flexural Stress | ISO 178 | ||
| Compression Molded | 70.0 to 90.0 | MPa | |
| Injection Molded | 90.0 to 110 | MPa | |
| Compressive Stress | 200 to 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| Compression Molded | 1.5 to 3.5 | kJ/m² | |
| Injection Molded | 2.0 to 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| Compression Molded | 4.0 to 6.0 | kJ/m² | |
| Injection Molded | 6.0 to 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 160 to 180 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 100 to 120 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 150°C) | 2.5E-5 to 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 to 0.40 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 to 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 to 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 20 to 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 16.0 12.0 | ||
| 1 MHz | 6.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.60 to 0.80 | ||
| 1 MHz | 0.060 to 0.080 | ||
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index | > 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.60 mm, Tested by Synres-Almoco) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 900 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 900 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 134502 | RTP Company | PP, Unspecified | RTP |
| Fusabond® M623XF | DuPont Packaging & Industrial Polymers | PE Copolymer | Fusabond® |
| ESENTTIA 60C55ND | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |
| LNP™ LUBRICOMP™ FX86496 compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ LUBRICOMP™ |
| Lupoy® EU5000G | LG Chem Ltd. | ASA+PC | Lupoy® |