HANWHA LDPE 5301
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DCzHp1_HANWHA-LDPE-5301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LDPE 5301 is manufactured by DOW tubular high pressure process and designed for variety of film application such as shrink, heavy duty and greenhouse film. LDPE 5301 has well balanced property of heat shrink, mechanical property and processability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 17.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 80 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 80 µm | 27.5 | MPa | ASTM D882 |
| TD : Broken, 80 µm | 23.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 80 µm | 110 | % | ASTM D882 |
| TD : Broken, 80 µm | 95 | % | ASTM D882 |
| Dart Drop Impact (80 µm) | 250 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 80.0 µm | 343.2 | kN/m | ASTM D1004 |
| TD : 80.0 µm | 588.4 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 |
| Melting Temperature | 110 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (80.0 µm) | 16 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.05 to 0.2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AX10WT6393 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| TOTAL Polypropylene PPR 3727W | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Arnite® TV4 290 | DSM Engineering Plastics | PBT | Arnite® |
| HiFill庐 PA6 GF20 RM BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Hostacom PC072-3 NATRL | LyondellBasell Industries | PP Homopolymer | Hostacom |