Nycal™ 2150R33T2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Nycal™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DCDB07_Nycal-2150R33T2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nycal™2150R33T2 is a polyamide 66 (nylon 66) material, which contains a 33% glass fiber reinforced material. This product is available in North America and is processed by injection molding. Nycal™The main features of 2150R33T2 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 148 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 7580 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 254 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 249 | °C | ASTM D648 |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Tensile Elongation, ASTM D638: 3 to 5%Volum Resistivity, ASTM D257: >1e14 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 - 79.4 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 277 - 304 | °C | |
| Mold Temperature | 65.6 - 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperLite® SL551600-100 (7.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Badaflex® TPE-S 45A 1000LD | Bada AG | TPE | Badaflex® |
| Haysite BMC 30000 | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| I. Stern 870E | I. STERN & CO. INC. | PS (HIPS) | I. Stern |