RAMOFIN PPH501G4
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMOFIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DC0lWs_RAMOFIN-PPH501G4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber 20% Reinforced, Halogen Free, Flame Retardant Polypropylene for Injection Moulding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.40 | % | ASTM D955 |
| -- | 0.20 to 0.40 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4280 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 65.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 3500 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 100 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 167 | °C | ISO 11357-3, ASTM D3417 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | 850 | °C | IEC 60695-2-13 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® BF40 LN | NUREL, S.A. | Nylon 6 | Promyde® |
| Taitacell EPS 321MM | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Ultramid® B3EG6 BK00564 | BASF Corporation | Nylon 6 | Ultramid® |
| Utomer UT81P90A | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyether | Utomer |
| LNP™ COLORCOMP™ 325C compound | SABIC Innovative Plastics | PBT | LNP™ COLORCOMP™ |