TABOREX TA 1121 HD
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SILON s.ro |
| Trademark: | TABOREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DA1z5t_TABOREX-TA-1121-HD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A chemically-crosslinkable HDPE compound for the production of pipes for domestic hot and cold water, under floor heating and central heating application. TA 1121 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a "SIOPLAS-SYSTEM". Pipes produced with the SILON grade TA 1121 HD fulfil the requirements of ASTM F876-99a, ASTM F877-99a, CSA 137.5-99, DIN 16892 and all related standards. This system allows the compound to be extruded as a normal thermoplastic polymer, which will attain a high level of crosslinking in the processed form. The final product has all the improved properties associated with crosslinked polyethylene. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | Internal method |
| Apparent Density | 0.54 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 1.0 | g/10 min | Internal method |
| Volatile Matter | % | Internal method | |
| Gel Content | 71 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 28.0 | MPa | Internal method |
| Tensile Strain (Break) | 470 | % | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 160 - 170 | °C | |
| Cylinder Zone 2 Temp. | 170 - 180 | °C | |
| Cylinder Zone 3 Temp. | 170 - 190 | °C | |
| Cylinder Zone 4 Temp. | 170 - 190 | °C | |
| Die Temperature | 190 - 220 | °C |
| Extrusion instructions |
|---|
| L/D: >25Compression ratio: 3:1 to 2.5 : 1Head: 200 to 210°CScrew: 70°C to 90 °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LC 185 A | A. Schulman Europe | ABS | POLYMAN® |
| Toyolac® 532-X02 | Toray Resin Company | ABS | Toyolac® |
| Bynel® 3126 | DuPont Packaging & Industrial Polymers | EVA | Bynel® |
| Duratron® T5530 | Quadrant Engineering Plastic Products | PAI | Duratron® |
| Huafon JF-W-AL6050 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |