Wanthane® WHT-1185F
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Wanhua Chemical Group Co., Ltd. |
| Trademark: | Wanthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D9LUoR_WanthaneWHT1185F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TYPE: Polyester-based grade Extrusion and injection grade FEATURES: Excellent mechanical properties, good extrusion stability, good low-temperature flexibility, outstanding wear resistance. APPLICATIONS: Hoses, spiral tubes, screenpacks, technical parts, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 89 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| DIN Abrasion | 35.0 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 6.00 | MPa | ASTM D412 |
| 300% strain | 12.0 | MPa | ASTM D412 |
| Tensile Strength (Break) | 39.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 570 | % | ASTM D412 |
| Tear Strength | 118 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | ASTM D3418 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 190 | °C | |
| Middle Temperature | 195 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 205 | °C | |
| Mold Temperature | 23 | °C | |
| Screw L/D Ratio | 25.0:1.0 to 30.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Cylinder Zone 1 Temp. | 185 | °C | |
| Cylinder Zone 2 Temp. | 190 | °C | |
| Cylinder Zone 3 Temp. | 195 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Adapter Temperature | 205 | °C | |
| Die Temperature | 195 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trexprene® A74NU | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Chemical Resources ABS700 | Chemical Resources, Inc. | ABS | Chemical Resources |
| Hanwha Total PE P200Y50 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| IROGRAN® A 85 E 4607 E | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Karina CLEAR PVC COMPOUND 80/210-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |