TEKAMID™ TA210L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D7RpBC_TEKAMID-TA210L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TEKAMID™ TA210L is a Polyamide 66 (Nylon 66) product. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 1.5 | % | |
| Across Flow | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 83.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 3040 | MPa | ASTM D790 |
| Flexural Strength | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 235 | °C | |
| 1.8 MPa, Unannealed | 90.0 | °C | |
| Peak Melting Temperature | 260 | °C | ASTM D2133 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 5.0 to 10 | hr | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 260 to 290 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 44.1 to 152 | MPa |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 118W | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Topolymer® 5211-951E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| ALCOM® PA6 900/1 MO1 | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Grivory® HT XE 4027 nat | EMS-GRIVORY | Nylon 10T/X | Grivory® |
| ICORENE® 1506 BLACK 9001 | A. Schulman Europe | XLPE | ICORENE® |